Ready-to-use adhesive mortar for lining KALFIX C30

KALFIX Manufacturer: Kalenborn

Ready-to-use adhesive mortar for lining KALFIX C30

KALFIX C30 is a ready-to-use adhesive mortar for laying and grouting joints on wear-resistant mineral, ceramic, and metal materials.

Material
Adhesives and compounds
Base
Cement
System
Ready-mixed mortar
Max. service temperature
150 °C

Made to order Price on request

Documents
Industrial adhesives

Specifications

General
Material Adhesives and compounds
Base Cement
System Ready-mixed mortar
Purpose Laying wear-resistant linings
Physical and mechanical properties
Max. service temperature, °C 150
Application and installation
Pot life 2–3 h at 20 °C
Curing time Min. 3 days at 20 °C
Ready for service After 3–7 days at 20 °C
Layer thickness, mm 10–30
Joint width, mm 3–6
Supply and storage
Packaging Bags

Description

Download the technical data sheet for ready-to-use adhesive mortar KALFIX C30

Ready-to-use adhesive mortar KALFIX C30 is designed for laying linings and grouting joints on mineral, ceramic and metal wear-resistant materials.

KALFIX C30 is a ready-to-use Portland cement-based mortar with rapid initial hardening and medium to high strength, supplied in bags.

The KALFIX C30 formulation ensures optimum laying results and high-quality fixing of the lining.

Product specifications:

Property Unit Value
Working time after mixing h (at 20 °C) 2–3
Curing time after application days (at 20 °C) min. 3
Putting the component into service
(depending on the application)		 days (at 20 °C) after 3–7
Bed thickness mm 10–30
Joint width mm 3–6
Maximum service temperature °C 150

Owing to the nature of the manufacturing process, product properties may vary. This includes features typical of hydraulically setting mortars, for example those caused by temperature and conditions of use, as well as variations in product properties relating to application and curing.

Key advantages

  • Ready-to-use Portland cement-based mortar - no component selection required, supplied in bags
  • Rapid initial hardening, ready for service after 3-7 days at 20 °C
  • Bed thickness 10-30 mm, joint width 3-6 mm
  • Service temperature up to 150 °C
  • Suitable for laying linings and grouting joints on mineral, ceramic and metal wear-resistant materials

Applications

KALFIX C30 is used to install wear-resistant linings in components exposed to abrasive wear: troughs, hoppers, chutes, cyclones and equipment housings. The ready-mixed cement-based compound is convenient for laying tiles and grouting joints on concrete and metal substrates, with no need to select components on site.

KALFIX C30 is a hydraulically setting mortar, so property variations typical of such materials may occur depending on temperature and application conditions. Mixing and laying are carried out at ambient temperatures from +5 to +30 °C (the values in the table are given for 20 °C), the working time of 2-3 hours after mixing with water must be observed, and the bond reaches full strength as it cures.

Documents

Frequently asked questions

For laying wear-resistant linings and grouting joints on mineral, ceramic and metal materials. It is a ready-to-use Portland cement-based adhesive mortar.

The maximum service temperature is up to 150 °C.

Bed thickness 10-30 mm, joint width 3-6 mm.

Yes, only with water: KALFIX C30 is a ready-to-use Portland cement-based dry mix that is mixed with water at a ratio of 6:1 by weight (KALFIX C30 : water). After mixing with water, the working time is 2-3 hours at 20 °C.

Approximately after 3-7 days at 20 °C, depending on the application; the minimum curing time is 3 days.

For mineral, ceramic and metal wear-resistant materials; the mortar provides reliable fixing of the lining and high-quality joint grouting on concrete and metal substrates.